Adiffusion couple of two metals, a and b, was fashioned as shown in figure 5.1. after a 26 hour heat treatment at 1050°c (and subsequent cooling to room temperature) the concentration of a is 4.0 wt% at the 14-mm position within metal b. if another heat treatment is conducted on an identical diffusion couple, only at 711°c for 26 hours, at what position (in mm) will the composition be 4.0 wt% a? the preexponential and activation energy values for the diffusion of a in b are 2.4 × 10-4 m2/s and 154 kj/mol, respectively.

1.25 mm

Explanation:

Given:

Temperature = 1050°C = 1050 + 273 = 1323 K

concentration of A = 4.0 wt%

preexponential value for the diffusion, D₀ = 2.4 × 10⁻⁴ m²/s

activation energy value for the diffusion, = 154 kJ/mol = 154 × 10³ J/mol

Diffusion coefficient at 1050°C , D₁₀₅₀ =

here,

R is the ideal gas constant = 8.314 J/mol·K.

T is the temperature

Thus

D₁₀₅₀ =

or

D₁₀₅₀ = 1.98 × 10⁻¹⁰

and,

Diffusion coefficient at 711°C , D₇₁₁ =

D₇₁₁ =

or

D₇₁₁ = 1.58 × 10⁻¹²

also,

 = constant

here, x is the position

thus,

or

or

x₇₁₁ = 1.25 mm

area of focus

as we probably am aware that our atmosphere or air have various levels, each level has different gasses, and each gas has another porousness. at the point when the light originates from lower porousness to higher penetrability, it alters its course. with the goal that implies that when the light originates from the moon to the earth, it alters it's course a lot more occasions. it essentially implies that the state of the light piece of the moon is changed on the earth.